Basic Info.
Model NO.
BH-4330
Fiber Characteristics
E-Glass
Diameter of Filaments
Advanced Fibers
Fiber Appearance
Continous Fiber
Glass Composition
E-Glass
Shape
Chopped
Transport Package
Pallet
Specification
6mm
Trademark
Beihai
Origin
China
Production Capacity
10000/Month
Packaging & Delivery
Package Size
20.00cm * 30.00cm * 12.00cm
Package Gross Weight
1.000kg
Product Description
Phenolic Fiberglass Molding Plastics
This series of products are thermosetting molding plastics made of e-glass fiber and modified phenolic resin by soaking and baking. It is used for pressing heat-resistant, moisture-proof, mildew proof, high mechanical strength, good flame retardant insulating parts, but also according to the requirements of the parts, the fiber can be properly combined and arranged, with high tensile strength and bending strength, and suitable for wet conditions.
- Good Mechanical Properties: Our products boast excellent mechanical properties, ensuring durability and reliability in various applications.
- Electrical Insulation: With superior electrical insulation, our products offer enhanced safety and protection.
- Arc Resistance and Anti-Static: Our products are specifically engineered to resist arcs and prevent static electricity, making them ideal for sensitive environments.
- Good Corrosion Resistance: Our products exhibit remarkable resistance to corrosion, including acid, alkali solutions, and other chemicals.
- Lightweight and High Product Utilization: Designed to be lightweight, our products offer ease of use and maximum product utilization.
- Strong Designability: Our products provide flexibility in design, allowing for customization and adaptability to various requirements.
- Widely Used: Our products find extensive applications across industries due to their versatility and reliability.
| NO. | Test Items | Unit | Index | Test |
| 1 | Resin Content | % | Customized | 38.6 |
| 2 | Volatile Matter Content | % | 3.0-6.0 | 3.87 |
| 3 | Density | g/cm3 | 1.65-1.85 | 1.9 |
| 4 | Water Absorption | mg | ≤20 | 15.1 |
| 5 | Martin Temperature | ºC | ≥280 | 290 |
| 6 | Bending Strength | MPa | ≥160 | 300 |
| 7 | Impact Strength | KJ/m2 | ≥50 | 130 |
| 8 | Tensile Strength | MPa | ≥80 | 180 |
| 9 | Surface Resistivity | Ω | ≥10x10^11 | 10x10^11 |
| 10 | Volume Resistivity | Ω.m | ≥10x10^11 | 10x10^11 |
| 11 | Medium wearing factor (1MHZ) | - | ≤0.04 | 0.03 |
| 12 | Relative Permittivity (1MHZ) | - | ≥7 | 11 |
| 13 | Dielectric Strength | MV/m | ≥14.0 | 15 |
It is suitable for pressing mechanical components with high strength, electrical components with complex shape, radio parts, mechanical parts and electrical parts with high strength and commutator (commutator), etc. Its products also have good electrical performance, especially suitable for hot and humid areas.
It should be stored in a dry and ventilated room where the temperature does not exceed 30ºC.
Do not close to fire, heating and direct sunlight, erect stored on a special platform, horizontal stacking and heavy pressure are strictly prohibited.
Shelf life is two months from the date of production. After the storage period, the product can still be used after passing the inspection according to the product standards. Technical standard: JB/T5822-2015