Fiberglass Biaxial Core Complex It is made of continuous roving oriented in 0,90 directions plus sunthetic core and chopped strand bonded with stitching ployester .
It is ideal for infusion process.
General Data
Code |
Weight (g/m2) | Chopped layer (g/m2) | PP Core layer(g/m2) | Moisture content | Wet speed (≤S) |
S300/180/300 | 780 | 300/300 | 180 | ≤0.2 | ≤60 |
S450/180/450 | 1080 | 450/450 | 180 | ≤0.2 | ≤60 |
S600/180/600 | 1380 | 600/600 | 180 | ≤0.2 | ≤60 |
S750/180/750 | 1680 | 750/750 | 180 | ≤0.2 | ≤60 |
S300/250/300 | 850 | 300/300 | 250 | ≤0.2 | ≤60 |
S450/250/450 | 1150 | 450/450 | 250 | ≤0.2 | ≤60 |
S600/250/600 | 1450 | 600/600 | 250 | ≤0.2 | ≤60 |
S750/250/750 | 1750 | 750/750 | 250 | ≤0.2 | ≤60 |
Roll width: Standard width in 1250mm, 1270mm, and other sizes depends on customer's real needs, available in 200mm to 3200mm.
Packing: Fiberglass chopped core mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15ºC to 35ºC and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.